Non-Ferrous Solutions

HTB

TiB2

A hard coating with a low coefficient of friction, recommended for high silicon aluminum alloys, titanium alloys, magnesium alloys, no lead brass, bronze and copper alloys.

Microhardness

4000 HV

Coefficient of Friction

0.10–0.20

Oxidation Temperature

850°C / 1562°F

Thickness

1-2 µm (based on tool diameter)

Unmatched durability recommended for applications in:

  • Alumiunum alloys
  • Titanium alloys
  • Magnesium alloys
  • Copper alloys
  • Graphite machining
Request Quote
HDT

TiAlSiN

HDT is engineered to perform in a diverse range of applications; from alloy steels to hardened materials and titanium.  HDT is exceptional for applications requiring high material removal rates by providing excellent wear resistance and high thermal resistance.

Microhardness

3600 HV

Coefficient of Friction

0.45

Oxidation Temperature

1150°C / 2100°F

Thickness

1-5 µm (based on tool diameter)

High performance solution for applications including:

  • Alloy steels
  • Hardened materials
  • Titanium alloys
  • Super alloys
Request Quote
HTC

TiCN

Lower coefficient of friction compared to HTN. A lubricious coating and with proper post treatment it is useful in stamping, forming and tapping operations, as well as the machining of non-ferrous materials.

Microhardness

3000 HV

Coefficient of Friction

0.30–0.45

Oxidation Temperature

400°C / 752°F

Thickness

1-5 µm (based on tool diameter)

Lubricious coating recommended for applications in:

  • Low tensile strength stamped metals
  • Low carbon steels
  • Non-ferrous materials
Request Quote